In industrial process facilities, corrosion is the biggest single cause of plant and equipment breakdown, including machinery, vessels, structures, supports, and pipelines. While atmospheric corrosion in the form of air (oxygen), and water (moisture, humidity, vapor, etc.) is the main culprit, environmental factors including high temperatures and pressures as well as harsh substances, chemicals, and gasses can also accelerate the corrosion of carbon steel and other metals in these facilities. Corrosion protection is key in these situations.
Beyond marine environments exposed to salt spray or compounds that cause corrosion, common gaseous industrial air pollutants, such as sulfur dioxide, ozone, and nitrogen dioxide, can be corrosion inducing. So can exposure to industrial chemicals such as chlorides, acetic acid, and formaldehyde.
“There is a huge need for an anti-corrosion coating that can go on in areas where conventional coatings tend to fail,” says Joey Taylor, President of IPI Inc., an Elkview WV-based paint/coating contractor for commercial and industrial construction. “On certain projects, chlorides need to be removed in order to meet peak performance. But in most cases, this can be cost-prohibitive.”
For industrial facilities with assets prone to environmental corrosion, a new category of tough, Chemically Bonded Phosphate Ceramic (CBPC) coatings is helping to stop corrosion, ease application, and reduce production downtime.
Long-Term Environmental Corrosion Protection
When aluminum is recycled, it is melted to separate the pure metal from the impurities. The process creates a waste product called salt cake, which contains compounds that can promote corrosion.
As a result, typical barrier-type anti-corrosion coatings, such as polymer paints, can fail prematurely. This is particularly true when the paint is scratched, chipped, or breached and corrosion promoters enter the gap between the substrate and coating. Then the coating can act like a greenhouse — trapping the corrosion promoters — that allows the corrosion to spread under the coating.
So, when an aluminum recycling plant in West Virginia required corrosion protection for its operation, it sought a long-term term solution that would not require frequent recoating, according to Taylor, who was involved with the project.
“The recycling plant was not having much luck with conventional anti-corrosion coatings, which only lasted about three or four years,” says Taylor. “Really, anyone trying to protect their assets from corrosion wants their coating to last much longer than that.”
To provide long-term corrosion protection in a tough environment, the aluminum recycling plant and Taylor turned to EonCoat, a spray applied inorganic coating from the Raleigh, NC-based company of the same name. EonCoat represents a new category of rugged, Chemically Bonded Phosphate Ceramics (CBPCs) with distinct characteristics.
In contrast to traditional polymer coatings that sit on top of the substrate, the corrosion resistant CBPC coating bonds through a chemical reaction with the substrate. The coating can even be applied over flash rusted, damp steel. An alloy layer is formed. This prevents corrosion promoters (like oxygen and humidity) from getting behind the coating the way they do with ordinary paints.
Although traditional polymer coatings mechanically bond to substrates that have been extensively prepared, if gouged, moisture and oxygen will migrate under the coating’s film from all sides of the gouge.
By contrast, the same damage to the ceramic-coated substrate will not spread corrosion in industrial infrastructure because the carbon steel’s surface is turned into an alloy of stable oxides. Once the steel’s surface is stable (the way noble metals like gold and silver are stable) it will no longer react with the environment and cannot corrode.
Visible in scanning electron microscope photography, EonCoat does not leave a gap between the steel and the coating because the bond is chemical rather than mechanical. Since there is no gap, even if moisture was to get through to the steel due to a gouge, there is nowhere for the moisture to travel, which effectively stops corrosion in industrial applications.
The corrosion barrier is also covered by a ceramic layer that resists corrosion, water, impact, abrasion, and chemicals as well as fire and temperatures up to 450°C (842°F).
For corrosion protection at the above mentioned aluminum recycling plant, IPI Inc. sprayed EonCoat on two industrial dust collectors (one 60,000 CFM and one 40,000 CFM), including four tanks as large as 40 feet tall and associated ductwork, according to IPI’s Taylor. “The CBPC anti-corrosion coating is designed to last significantly longer than traditional coatings, so frequent recoating should not be an issue,” he says.
Applying The Corrosion Protection Product
Industrial operation managers or corrosion engineers looking to reduce costs are also finding additional advantages with CBPC coatings like EonCoat beyond corrosion resistance.
Such coatings consist of two non-hazardous components that do not interact until applied with a standard industrial plural spray system like those commonly used to apply polyurethane foam or polyurea coatings. Since CBPC coatings are inorganic and non-toxic, there are no VOCs, no HAPs, and no odor. This means the water soluble, non-flammable coatings can be applied safely in confined spaces, or when adjacent parts of a plant continue to operate.
“With the CBPC coating, since there are no VOCs or odor, coating can be done around plant employees or other contractors without restrictions,” says Taylor.
Another benefit is a quick return to service that minimizes facility downtime. The time saved on anti-corrosion coating projects comes both from simplified surface preparation and expedited curing time. With a typical industrial coating, near white metal blast cleaning (NACE 2 / SSPC-SP 10) is required to prepare the surface. With the ceramic coating, only a NACE 3 / SSPC-SP 6 commercial blast cleaning is typically necessary.
With traditional coatings, extensive surface preparation is required and done a little at a time to avoid surface oxidation, commonly known as ‘flash rust’, which can require re-blasting.
With the CBPC coating, flash rust is no issue. There is no need to ‘hold the blast’. The reason for this unique CBPC characteristic is due to the presence of iron in the rust, which helps to create the magnesium iron phosphate alloy layer. It is this alloy layer that allows CBPCs to effectively protect carbon steel from corrosion.
“Conventional coatings require you to prime the substrate every day so you do not lose your blast,” says Taylor. “You have to stop sandblasting in the early afternoon, and then prime the rest of the day. This requires time-consuming daily teardown and set up of paint equipment.”
“With EonCoat, however, once you have a clean substrate surface, free of mill scale and coating, it will not hurt it to let it flash rust,” adds Taylor. “So, you can continue coating without having to re-blast the substrate, re-prime it, or set up and teardown paint equipment each day. You can continue to blast the entire 12-hour shift. That saved us about a 50-hour workweek on the project.”
For traditional “three-part system” coatings utilizing polyurethanes or epoxies, the cure time may also be days or weeks before the next coat can be applied, depending on the product.
In contrast, a corrosion resistant coating for carbon steel, utilizing the ceramic coating in a single coat, requires almost no curing time.
Industrial facility managers looking for more reliable, long-term corrosion protection in harsh environments might consider CBPC coatings.
“We were able to complete the project from start to finish in nine weeks, including substrate preparation, spraying, and adding a high-performance topcoat with minimal disruption to the plant’s operations,” says Taylor.